Select a backing to see Specifications
| Product Construction |
Tufted Textured Loop |
| Yarn System |
100% Solution Dyed Nylon |
| Yarn Manufacturer |
Universal |
| Dye Method |
100% Solution Dyed |
| Soil/Stain Protection |
Protekt²® |
| Preservative Protection |
Intersept® |
| Imperial | Metric | |
|---|---|---|
| Tufted Pile Weight |
12.00 oz/yd² |
407.00 g/m2 ± 5% |
| Machine Gauge |
1/12 in |
47.2 ends/10cm |
| Stitches |
10.91 in |
43.00 ends/10cm |
| Pile Thickness |
0.12 in |
3.00 ±0.5 mm |
| Total Thickness |
0.217 in |
5.5 mm ±0.5 mm |
| Size Description |
19.69 in x 19.69 in |
50 x 50 cm |
| Area of Use |
Commercial - Heavy Use |
| Stability - Delaminating |
ASTM D3936 ≥ 2.5lbs/in AS/NZS 2111.16 ≥ 50 Newtons |
| Stability - Dimensional Stability |
ISO 2551 ≤ 0.2% ISO/PAS 17984 < 0.2% |
| Stability - Tuft Bind |
AS/NZS 2111.15 >30 Newtons ASTM D1335 ≥ 8.0lbs |
| Wear - Castor Chair |
BS-EN 985 r ≥ 2.4 |
| Wear - Vetterman Drum |
ISO 10361 (ASTM D5417) ≥ 3.5 Rating @20,000 cycles |
| Colour Fastness to Light |
AS2001.4.21 ≥ 4 |
| Colour Fastness to Rubbing and Crocking |
AATCC 165 ≥ 4 AS/NZS2111.19.1 ≥ 4 |
| Colour Fastness to Water |
AATCC 107 ≥ 4 AS2001.4.21 ≥ 4 |
| Flammability - Radiant Panel |
ISO 9239-1 B1 |
| Flammability - Smoke density |
ISO 9239-1 Density < 750 %.min |
| Antistatic |
BS ISO 6356 ≤ 2.0Kv |
| Acoustic - Nylon |
Absorption Coefficient - NRC ≥ 0.10 |
| Dynamic Loading |
AS/NZS 2111.2 < 12.5% loss ISO 2094 ≥ 85% |
| Green Carpet (VOC) |
ASTM D5116 Accredited ISO 10580 Accredited |
| Static Loading |
AS/NZS2111.13 < 6% Loss ISO 015/3415 Thickness after 60 mins recovery >85% |
| Thermal Resistance |
ASTM C518 R Value ≥ 0.5 |
| Recycled Content % |
59 % |
| Pre-Consumer (Total) |
57.00 % |
| Post-Consumer (Total) |
2.00 % |
| Ingredients and Life Cycle Impacts | |
| Other Environmental Claims | |
| End of Life |
Carpet to Carpet Recycling |
| Embodied Carbon (Cradle to Gate) |
4.9 kg CO₂ eq./m² |
| Installation | |
| Maintenance | |
| Reclamation | |
| Warranty | |
| Manufacturing Location |